Ultem
1000
|
Ultem
1000
|
Ultem
2300
|
Ultem
2300
|
Semitron
ESD410
|
|
|
|
|
Units
|
ASTM
Test Method
|
Extruded
Polyetherimide
|
Injection
molded Polyetherimide
|
Extruded
30% Glass Filled Polyetherimide
|
Injection
Molded 30% GF Polyetherimide
|
Static
Dissapative Polyetherimide
|
|
MECHANICAL
|
1
|
Strength
to Weight Ratio
|
ksi
|
-
|
|
|
|
|
|
|
2
|
Specific
Gravity @73 F
|
-
|
D792
|
1.28
|
1.27
|
1.51
|
1.51
|
1.41
|
|
3
|
Tensile
Strength @73 F, (ult)/(yld)
|
psi
|
D638
|
16500
(ult)
|
15200
(yld)
|
17000
(ult)
|
24500
(yld)
|
9000
|
|
4
|
Tensile
Modulus of Elasticity @ 73 F
|
psi
|
D638
|
475000
|
-
|
800000
|
1260000
|
850000
|
|
5
|
Tensile
Elongation at Break @ 73 F
|
%
|
D638
|
80
|
7
|
3
|
3
|
2
|
|
6
|
Flexural
Strength @ 73 F
|
psi
|
D790
|
20000
|
22000
|
30000
|
33000
|
12000
|
|
7
|
Flexural
Modulus of Elasticity @ 73 F
|
psi
|
D790
|
500000
|
480000
|
900000
|
1300000
|
850000
|
|
8
|
Shear
Strength @ 73 F
|
psi
|
D732
|
15000
|
15000
|
-
|
14000
|
-
|
|
9
|
Compressive
Strength, (% Deformation) @73 F
|
psi
|
D695
|
22000
(10)
|
21900
(10)
|
32000
(10)
|
30700
(10)
|
19500
(10)
|
|
10
|
Compressive
Modulus of Elasticity @73 F
|
psi
|
D695
|
480000
|
480000
|
625000
|
938000
|
600000
|
|
11
|
Hardness,
Rockwell, Scale as noted @73 F
|
-
|
D785
|
M112
(R125)
|
M109
|
M114
(R127)
|
M114
|
M115
(R125)
|
|
12
|
Hardness, Durometer,
Shore D @73 F
|
-
|
D2240
|
D86
|
-
|
D86
|
-
|
D85
|
|
13
|
Izod
Impact, (Notched) @73 F
|
ft-lb/in
of notch
|
D256
TypeA
|
0.5
|
1.0
|
1.0
|
2.0
|
0.8
|
|
14
|
Coefficient
of Friction, (Dry vs. Steel) Dynamic
|
-
|
-
|
0.42
|
-
|
-
|
-
|
0.18
|
|
15
|
Limiting
PV, (with 4 to 1 factor of safety applied)
|
psi-ft/min
|
-
|
1875
|
-
|
-
|
-
|
12000
|
|
THERMAL
|
16
|
Coefficient
of Linear Thermal Expansion @73 F
|
in/in/F
|
E-831
(TMA)
|
3.1E-05
|
3.1E-05
|
1.1E-05
|
1.1E-05
|
1.8E-05
|
|
17
|
Heat
Deflection Temperature @ 264 psi
|
F
|
D648
|
392
|
392
|
410
|
410
|
410
|
|
18
|
Tg-Glass
transition temperature, (Amorphous)
|
F
|
D3418
|
419
|
-
|
419
|
-
|
428
|
|
19
|
Melting
Point, (VS=Vicat Softening Temp.)
|
F
|
D3418
|
-
|
-
|
-
|
442
(VS)
|
-
|
|
20
|
Continuous
Service Temperature in Air, (Max.)
|
F
|
-
|
340
|
340
|
340
|
340
|
338
|
|
21
|
Thermal
Conductivity
|
BTU-in/hr-ft2-F
|
-
|
0.90
|
.22
W/M-C
|
1.15
|
-
|
-
|
|
ELECTRICAL
|
22
|
Dielectric
Strength, Short Term
|
Volts/mil
|
D149
|
830
|
830
|
770
|
770
|
-
|
|
23
|
Volume
Resistivity
|
ohm-cm
|
D257
|
6.7E+17
|
1.0E+17
|
3.0E+16
|
3.0E+16
|
1E5-1E7
|
|
24
|
Dielectric
Constant @ 10E6 Hz
|
-
|
D150
|
3.2
|
-
|
3.7
|
-
|
-
|
|
25
|
Dissipation
Factor @ 10E6 Hz
|
-
|
D150
|
0.001
|
-
|
0.002
|
-
|
-
|
|
26
|
Flammability @
3.1 mm unless noted
|
-
|
UL94
|
V-0
|
5VA(1.9mm)
|
V-0
|
V-0
(.25mm)
|
V-0
|
|
H2O
|
27
|
Water
Absorbtion, Immersion, 24 Hrs
|
%
by wt.
|
D570(7)
|
0.25
|
0.25
|
0.18
|
0.16
|
0.30
|
|
28
|
Water
Absorbtion, Saturation
|
%
by wt.
|
D570(7)
|
1.25
|
1.25
|
.90
|
.90
|
1.25
|