Ketron
PEEK
|
Victrex
PEEK 450G
|
Ketron
PEEK
|
30%
Glass Filled Ketron PEEK
|
30%
Glass Filled Ketron PEEK
|
Victrex
PEEK 450GL30
|
30%
Carbon Filled Ketron PEEK
|
30%
Carbon Filled Ketron PEEK
|
Victrex
PEEK 450CA30
|
Ketron
PEEK HPV
|
Victrex
PEEK Optima LT
|
|
|
|
|
Units
|
ASTM
Test Method
|
Compression
Molded Poly-etheretherketone
|
Injection
Molded Poly-etheretherketone
|
Extruded
Polyether-etherketone
|
Compression
Molded 30% GF PEEK
|
Extruded
30% Glass Filled PEEK
|
Injection
Molded 30% GF PEEK
|
Compression
Molded 30% CF PEEK
|
Extruded
30% Carbon Filled PEEK
|
Injection
Molded 30% CF PEEK
|
Bearing
Grade Polyether-etherketone
|
Injection
Molded Poly-etheretherketone
|
|
MECHANICAL
|
1
|
Strength
to Weight Ratio
|
ksi
|
-
|
|
|
|
|
|
|
|
|
|
|
|
|
2
|
Specific
Gravity @73 F
|
-
|
D792
|
1.32
|
1.30
|
1.31
|
1.45
|
1.54
|
1.50
|
1.42
|
1.41
|
1.41
|
1.44
|
1.30
|
|
3
|
Tensile
Strength @73 F, (ult)/(yld)
|
psi
|
D638
|
15000
(ult)
|
14100
(ult)
|
16000
(ult)
|
17000
(ult)
|
18000
(ult)
|
22620
(ult)
|
20000
(ult)
|
23200
(ult)
|
33785
(ult)
|
17400
|
14100
(ult)
|
|
4
|
Tensile
Modulus of Elasticity @ 73 F
|
psi
|
D638
|
450000
|
522000
|
500000
|
750000
|
1000000
|
1407000
|
800000
|
1400000
|
1885000
|
1100000
|
522000
|
|
5
|
Tensile
Elongation at Break @ 73 F
|
%
|
D638
|
1.0
|
5
|
20
|
3
|
3
|
2.0
|
2.0
|
3
|
2
|
3
|
5
|
|
6
|
Flexural
Strength @ 73 F
|
psi
|
D790
|
25000
|
24650
|
25000
|
28000
|
28000
|
33785
|
30000
|
-
|
51475
|
-
|
24650
|
|
7
|
Flexural
Modulus of Elasticity @ 73 F
|
psi
|
D790
|
600000
|
594500
|
600000
|
1000000
|
1000000
|
1450000
|
1300000
|
-
|
2929000
|
-
|
594500
|
|
8
|
Shear
Strength @ 73 F
|
psi
|
D732
|
-
|
7685
(ult)
|
8000
|
-
|
14000
|
14065
(ult)
|
-
|
-
|
14065
(ult)
|
-
|
7685
(ult)
|
|
9
|
Compressive
Strength, (% Deformation) @73 F
|
psi
|
D695
|
17000
(10)
|
17255
(10)
|
20000
(10)
|
19000
(10)
|
26000
(10)
|
31175
(10)
|
25000
(10)
|
29000
(10)
|
34800
(10)
|
21800
(10)
|
17255
(10)
|
|
10
|
Compressive
Modulus of Elasticity @73 F
|
psi
|
D695
|
450000
|
-
|
500000
|
500000
|
1000000
|
-
|
550000
|
-
|
-
|
-
|
-
|
|
11
|
Hardness,
Rockwell, Scale as noted @73 F
|
-
|
D785
|
M99
(R126)
|
M99
(R126)
|
M100
(R126)
|
M103
(R124)
|
M103
(R126)
|
M103(R124)
|
M97
(R125)
|
M104
|
M107
(R124)
|
M99
|
M99
(R126)
|
|
12
|
Hardness, Durometer,
Shore D @73 F
|
-
|
D2240
|
D85
|
-
|
D85
|
D86
|
D86
|
-
|
D86
|
-
|
-
|
-
|
-
|
|
13
|
Izod
Impact, (Notched) @73 F
|
ft-lb/in
of notch
|
D256
TypeA
|
1.0
|
1.6
|
1.0
|
1.4
|
1.4
|
1.8
|
1.4
|
1.0
|
1.6
|
0.7
|
1.6
|
|
14
|
Coefficient
of Friction, (Dry vs. Steel) Dynamic
|
-
|
-
|
0.40
|
-
|
0.40
|
-
|
-
|
-
|
0.19
|
-
|
-
|
0.24
|
-
|
|
15
|
Limiting
PV, (with 4 to 1 factor of safety applied)
|
psi-ft/min
|
-
|
12500
|
-
|
5500
|
-
|
-
|
-
|
25000
|
25000
|
-
|
13000
|
-
|
|
THERMAL
|
16
|
Coefficient
of Linear Thermal Expansion @73 F
|
in/in/F
|
E-831
(TMA)
|
2.6E-05
|
2.6E-05
|
2.6E-05
|
1.4E-05
|
1.2E-05
|
1.2E-05
|
1.7E-05
|
1.0E-05
|
8.0E-06
|
1.4E-05
|
2.6E-05
|
|
17
|
Heat
Deflection Temperature @ 264 psi
|
F
|
D648
|
320
|
306
|
320
|
600
|
600
|
600
|
600
|
518
|
600
|
446
|
306
|
|
18
|
Tg-Glass
transition temperature, (Amorphous)
|
F
|
D3418
|
-
|
289
|
-
|
-
|
-
|
289
|
-
|
289
|
289
|
289
|
289
|
|
19
|
Melting
Point, (VS=Vicat Softening Temp.)
|
F
|
D3418
|
644
|
644
|
644
|
644
|
644
|
644
|
644
|
644
|
644
|
644
|
644
|
|
20
|
Continuous
Service Temperature in Air, (Max.)
|
F
|
-
|
480
|
480
|
480
|
480
|
480
|
480
|
480
|
482
|
480
|
482
|
480
|
|
21
|
Thermal
Conductivity
|
BTU-in/hr-ft2-F
|
-
|
1.75
|
1.75
|
1.75
|
2.98
|
2.98
|
2.98
|
6.37
|
6.40
|
6.37
|
1.70
|
1.75
|
|
ELECTRICAL
|
22
|
Dielectric
Strength, Short Term
|
Volts/mil
|
D149
|
480
|
480
|
480
|
500
|
500
|
500
|
-
|
32
|
-
|
-
|
480
|
|
23
|
Volume
Resistivity
|
ohm-cm
|
D257
|
4.9E+16
|
4.9E+16
|
4.9E+16
|
5.0E+16
|
5.0E+16
|
1.0E+16
|
-
|
1.0E+06
|
1.4E+05
|
<1E8
|
4.9E+16
|
|
24
|
Dielectric
Constant @ 10E6 Hz
|
-
|
D150
|
3.3
|
3.3
|
3.3
|
-
|
-
|
3.7
|
-
|
-
|
-
|
-
|
3.3
|
|
25
|
Dissipation
Factor @ 10E6 Hz
|
-
|
D150
|
0.003
|
0.003
|
0.003
|
-
|
-
|
0.004
|
-
|
-
|
-
|
-
|
0.003
|
|
26
|
Flammability @
3.1 mm unless noted
|
-
|
UL94
|
V-0
|
V-0
|
V-0
|
V-0
|
V-0
|
V-0
|
V-0
|
V-0
|
V-0
|
V-0
|
V-0
|
|
H2O
|
27
|
Water
Absorbtion, Immersion, 24 Hrs
|
%
by wt.
|
D570(7)
|
0.15
|
0.50
|
0.10
|
0.15
|
0.10
|
0.11
|
0.15
|
0.06
|
0.06
|
0.05
|
0.50
|
|
28
|
Water
Absorbtion, Saturation
|
%
by wt.
|
D570(7)
|
0.50
|
0.50
|
0.50
|
0.50
|
0.30
|
-
|
0.50
|
0.30
|
-
|
0.30
|
0.50
|