PEEK Materials
CCT utilizes many different types of CNC equipment to produce parts for our customers. We have four CNC-controlled multi-spindled routers, five CNC controlled vertical machining centers, and one large format router. Our goal is to keep our personnel supplied with the equipment they need to produce parts to the most exacting tolerances. |
 |
Click here to close materials table.
| - | - | - | Ketron PEEK | Victrex PEEK 450G | Ketron PEEK | 30% Glass-filled Ketron PEEK | 30% Glass-filled Ketron PEEK | Victrex PEEK 450GL30 | 30% Carbon-filled Ketron PEEK | 30% Carbon-filled Ketron PEEK | Victrex PEEK 450CA30 | Ketron PEEK HPV | Victrex PEEK Optima LT |
| MECHANICAL | Units | ASTM Test Method | Compression Molded Polyetheretherketone | Injection Molded Polyetheretherketone | Extruded Polyetheretherketone | Compression Molded 30% GF PEEK | Extruded 30% GF PEEK- | Injection Molded 30% GF PEEK | Compression Molded 30% CF PEEK | Extruded 30% Carbon-filled PEEK | Injection Molded 30% CF PEEK | Bearing Grade Polyetheretherketone | Injection Molded Polyetheretherketone |
| Strength to Weight Ratio | ksi | - | - | - | - | - | - | - | - | - | - | - | - |
| Specific Gravity @73 F | - | D792 | 1.32 | 1.30 | 1.31 | 1.45 | 1.54 | 1.50 | 1.42 | 1.41 | 1.41 | 1.44 | 1.30 |
| Tensile Strength @73 F, (ult)/(yld) | psi | D638 | 15000 (ult) | 14100 (ult) | 16000 (ult) | 17000 (ult) | 18000 (ult) | 22620 (ult) | 20000 (ult) | 23200 (ult) | 33785 (ult) | 17400 | 14100 (ult) |
| Tensile Modulus of Elasticity @ 73 F | psi | D638 | 450000 | 522000 | 500000 | 750000 | 1000000 | 1407000 | 800000 | 1400000 | 1885000 | 1100000 | 522000 |
| Tensile Elongation at Break @ 73 F | % | D638 | 1.0 | 5 | 20 | 3 | 3 | 2.0 | 2.0 | 3 | 2 | 3 | 5 |
| Flexural Strength @ 73 F | psi | D790 | 25000 | 24650 | 2500 | 28000 | 28000 | 33785 | 30000 | - | 51475 | - | 24650 |
| Flexural Modulus of Elasticity @ 73 F | psi | D790 | 600000 | 594500 | 600000 | 1000000 | 1000000 | 1450000 | 1300000 | - | 2929000 | - | 594500 |
| Shear Strength @ 73 F | psi | D732 | - | 7685 (ult) | 8000 | - | 14000 | 14065 (ult) | - | - | 14065 (ult) | - | 7685 (10) |
| Compressive Strength, (% Deformation) @73 F | psi | D695 | 17000 (10) | 17255 (10) | 20000 (10) | 19000 (10) | 26000 (10) | 31175 (10) | 25000 (10) | 29000 (10) | 34800 (10) | 21800 (10) | 17255 (10) |
| Compressive Modulus of Elasticity @73 F | psi | D695 | 450000 | - | 500000 | 500000 | 1000000 | - | 550000 | - | - | - | - |
| Hardness, Rockwell, Scale as noted @73 F | - | D785 | M99 (R126) | M99 (R126) | M100 (R126) | M103 (R124) | M103 (R126) | M103 (R124) | M97 (R125) | M104 | M107 (R124) | M99 | M99 (R126) |
| Hardness, Durometer, Shore D @73 F | - | D2240 | D85 | - | D85 | D86 | D86 | - | D86 | - | - | - | - |
| Izod Impact, (Notched) @73 F | ft-lb/in of notch | D256 TypeA | 1.0 | 1.6 | 1.0 | 1.4 | 1.4 | 1.8 | 1.4 | 1.0 | 1.6 | 0.7 | 1.6 |
| Coefficient of Friction, (Dry vs. Steel) Dynamic | - | - | 0.4 | - | 0.40 | - | - | - | 0.19 | - | - | 0.24 | - |
| Limiting PV, (with 4 to 1 factor of safety applied) | psi-ft/min | - | 12500 | - | 5500 | - | - | - | 25000 | 25000 | - | 13000 | - |
| THERMAL | |||||||||||||
| Coefficient of Linear Thermal Expansion @73 F | in/in/F | E-831 (TMA) | 2.6E-05 | 2.6E-05 | 2.6E-05 | 1.4E-05 | 1.2E-05 | 1.2E-05 | 1.7E-05 | 1.0E-05 | 8.0E-06 | 1.4E-05 | 2.6E-05 |
| Heat Deflection Temperature @ 264 psi | F | D648 | 320 | 306 | 320 | 600 | 600 | 600 | 600 | 518 | 600 | 446 | 306 |
| Tg-Glass transition temperature, (Amorphous) | F | D3418 | - | 289 | - | - | - | 289 | - | 289 | 289 | 289 | 289 |
| Melting Point, (VS=Vicat Softening Temp.) | F | D3418 | 644 | 644 | 644 | 644 | 644 | 644 | 644 | 644 | 644 | 644 | 644 |
| Continuous Service Temperature in Air, (Max.) | F | - | 480 | 480 | 480 | 480 | 480 | 480 | 480 | 593 | 480 | 482 | 480 |
| Thermal Conductivity | BTU-in/hr-ft2-F | - | 1.75 | 1.75 | 1.75 | 2.98 | 2.98 | 2.98 | 6.37 | 6.40 | 6.37 | 1.70 | 1.75 |
| ELECTRICAL | |||||||||||||
| Dielectric Strength, Short Term | Volts/mil | D149 | 480 | 480 | 480 | 500 | 500 | 500 | - | 32 | - | - | 480 |
| Volume Resistivity | ohm-cm | D257 | 4.9E+16 | 4.9E+16 | 4.9E+16 | 5.0E+16 | 5.0E+16 | 1.0E+16 | - | 1.0E+06 | 1.4E+05 | <1E8 | 4.9E+16 |
| Dielectric Constant @ 10E6 Hz | - | D150 | 3.3 |
3.3 | 3.3 | - | - | 3.7 | - | - | - | - | 3.3 |
| Dissipation Factor @ 10E6 Hz | - | D150 | 0.003 | 0.003 | 0.003 | - | - | 0.004 | - | - | - | - | 0.003 |
| Flammability @ 3.1 mm unless noted | - | UL94 | V-0 | V-0 | V-0 | V-0 | V-0 | V-0 | V-0 | V-0 | V-0 | V-0 | V-0 |
| H2O | |||||||||||||
| Water Absorbtion, Immersion, 24 Hrs | % by wt. | D570(7) | 0.15 | 0.50 | 0.10 | 0.15 | 0.10 | 0.11 | 0.15 | 0.06 | 0.06 | 0.05 | 0.50 |
| Water Absorbtion, Saturation | % by wt. | D570(7) | 0.50 | 0.50 | 0.50 | 0.50 | 0.30 | - | 0.50 | 0.30 | - | 0.30 | 0.50 |