| MECHANICAL | Units | ASTM Test Method | Sumika Super S1000 |
| Strength to Weight Ratio | ksi | - | - |
| Specific Gravity @73 F | - | D792 | 1.35 |
| Tensile Strength @73 F, (ult)/(yld) | Mpa | D638 | 68.7 |
| Tensile Modulus of Elasticity @ 73 F | psi | D638 | - |
| Tensile Elongation at Break @ 73 F | % | D638 | 8 |
| Flexural Strength @ 73 F | Mpa | D790 | 100 |
| Flexural Modulus of Elasticity @ 73 F | Mpa | D790 | 3240 |
| Shear Strength @ 73 F | psi | D732 | - |
| Compressive Strength, (% Deformation) @73 F | Mpa | D695 | 144 (10) |
| Compressive Modulus of Elasticity @73 F | psi | D695 | - |
| Hardness, Rockwell, Scale as noted @73 F | - | D785 | R124 |
| Hardness, Durometer, Shore D @73 F | - | D2240 | - |
| Izod Impact, (Notched) @73 F | J/m of notch | D256 TypeA | 22 |
| Coefficient of Friction, (Dry vs. Steel) Dynamic | - | - | - |
| Limiting PV, (with 4 to 1 factor of safety applied) | psi-ft/min | - | - |
| THERMAL | |||
| Coefficient of Linear Thermal Expansion @73 F | in/in/F | E-831 (TMA) | - |
| Heat Deflection Temperature @ 1.82Mpa | C | D648 | 300 |
| Tg-Glass transition temperature, (Amorphous) | F | D3418 | - |
| Melting Point, (VS=Vicat Softening Temp.) | F | D3418 | - |
| Continuous Service Temperature in Air, (Max.) | C | - | 392 |
| Thermal Conductivity | BTU-in/hr-ft2-F | - | |
| ELECTRICAL | |||
| Dielectric Strength, Short Term | MV/m | D149 | 18 |
| Volume Resistivity | ohm/m | D257 | 1.0E+15 |
| Dielectric Constant @ 10E6 Hz | - | D150 | - |
| Dissipation Factor @ 10E6 Hz | - | D150 | - |
| Flammability @ 3.1 mm unless noted | - | UL94 | V-0 |
| H2O | |||
| Water Absorbtion, Immersion, 24 Hrs | % by wt. | D570(7) | 0.04 |
| Water Absorbtion, Saturation | % by wt. | D570(7) | 0.11 |